ZnO/TiO2 y ZnO/Nb2O5 como sistemas eficientes en el tratamiento de bacterias entéricas y colorantes comerciales

Autores/as

DOI:

https://doi.org/10.17533/udea.redin.20220785

Palabras clave:

ZnO/TiO2 o Nb2O5, Fotocatálisis, bacterias enteropatógenas, colorantes

Resumen

En esta investigación se evaluaron los óxidos mixtos ZnO/TiO2 y ZnO/Nb2O5 para la recuperación de agua de un río contaminado y en el tratamiento de aguas residuales de fábricas textiles; los contaminantes objeto de estudio en esta investigación fueron bacterias enteropatógenas y colorantes comerciales. Los sistemas conformados por óxidos mixtos fueron ampliamente caracterizados con el fin de conocer sus características fisicoquímicas; a partir de estos análisis se encontró que el acoplamiento de dos óxidos no modificó la cristalinidad de los semiconductores prístinos, pues, por DRX se identificaron las fases cristalinas wurtzita, anatasa y hexagonal para ZnO, TiO2 y Nb2O5, respectivamente. Mediante análisis de UV-Vis DRS se observó una mayor absorción de los óxidos mixtos en la región visible del espectro electromagnético, el valor de ancho de banda también disminuye en estos materiales. Los resultados de evaluación de la actividad fotocatalítica mostraron que el acoplamiento de ZnO con Nb2O5 y TiO2 aumenta la eficiencia en la eliminación del carbono orgánico total (COT) y de E. Coli. Con el fotocatalizador ZnO/TiO2 se logró la eliminación del 82% de COT y del 65% de E. coli, en muestras de agua de un río contaminado por efluentes municipales.

|Resumen
= 588 veces | PDF (ENGLISH)
= 272 veces| | HTML (ENGLISH)
= 0 veces| | XML (ENGLISH)
= 0 veces|

Descargas

Los datos de descargas todavía no están disponibles.

Biografía del autor/a

Jhon Sebastián Hernández-Niño, Universidad Pedagógica y Tecnológica de Colombia

Facultad de Ciencias, Magister

Julie Joseane Murcia-Mesa, Universidad Pedagógica y Tecnológica de Colombia

Doctora. Grupo de Catálisis, Facultad de Ciencias

Hugo Alfonso Rojas-Sarmiento, Universidad Pedagógica y Tecnológica de Colombia

Grupo de Catálisis, Facultad de Ciencias

María del Carmen Hidalgo, Universidad de Sevilla

Instituto de Ciencia de Materiales de Sevilla (ICMS), Consejo Superior de Investigaciones Científicas CSIC -

Jose Antonio Navío-Santos, Universidad de Sevilla

Instituto de Ciencia de Materiales de Sevilla (ICMS), Consejo Superior de Investigaciones Científicas CSIC

Citas

Progress on drinking water and sanitation: special focus on sanitation, World Health Organization, UNICEF, Geneva, SWE, 2008.

The Global Risks Report, 14th ed., World Economic Forum, Geneva, SWE, 2019.

J. Gamage-McEvoy and Z. Zhang, “Antimicrobial and photocatalytic disinfection mechanisms in silver-modified photocatalysts under dark and light conditions,” Journal of Photochemistry and Photobiology C: Photochemistry Reviews, vol. 19, Jun. 2014. [Online]. Available: https://doi.org/10.1016/j.jphotochemrev.2014.01.001

J. J. Murcia, E. G. Ávila-Martínez, H. Rojas, J. A. Navío, and M. C. Hidalgo, “Study of the E. coli elimination from urban wastewater over photocatalysts based on metallized tio2,” Applied Catalysis B: Environmental, vol. 200, Jan. 2017. [Online]. Available: https://doi.org/10.1016/j.apcatb.2016.07.045

A. Bernabeu, R. F. Vercher, L. Santos-Juanes, P. J. Simón, C. Lardín, and et al., “Solar photocatalysis as a tertiary treatment to remove emerging pollutants from wastewater treatment plant effluents,” Applied Catalysis B: Environmental, vol. 161, no. 1, Mar. 17, 2011. [Online]. Available: https://doi.org/10.1016/j.cattod.2010.09.025

S. Malato, P. Fernández-Ibáñez, M. I. Maldonado, J. Blanco, and W. Gernjak, “Decontamination and disinfection of water by solar photocatalysis: Recent overview and trends,” Catalysis Today, vol. 147, no. 1, Sep. 15, 2009. [Online]. Available: https://doi.org/10.1016/j.cattod.2009.06.018

C. Jaramillo-Páez, J. A. Navío, M. C. Hidalgo, and M. Macías, “High uv-photocatalytic activity of zno and ag/zno synthesized by a facile method,” Catalysis Today, vol. 284, Apr. 15, 2017. [Online]. Available: https://doi.org/10.1016/j.cattod.2016.11.021

V. Vaiano, C. A. Jaramillo-Paez, M. Matarangolo, J. A. Navío, and M. del C. Hidalgo, “Uv and visible-light driven photocatalytic removal of caffeine using zno modified with different noble metals (pt, ag and au),” Materials Research Bulletin, vol. 112, Apr. 2019. [Online]. Available: https://doi.org/10.1016/j.materresbull.2018.12.034

C. A. Jaramillo-Páez, J. A. Navío, M. C. Hidalgo, and M. Macías, “Zno and pt-zno photocatalysts: Characterization and photocatalytic activity assessing by means of three substrates,” Catalysis Today, vol. 313, Sep. 01, 2018. [Online]. Available: https://doi.org/10.1016/j.cattod.2017.12.009

J. M. Herrmann, “Heterogeneous photocatalysis: fundamentals and applications to the removal of various types of aqueous pollutants,” Catalysis Today, vol. 53, no. 1, Oct. 15, 1999. [Online]. Available: https://doi.org/10.1016/S0920-5861(99)00107-8

J. J. Murcia, A. C. Cely, H. A. Rojas, M. C. Hidalgo, and J. A. Navío, “Fluorinated and platinized titania as effective materials in the photocatalytic treatment of dyestuffs and stained wastewater coming from handicrafts factories,” Catalysts, vol. 9, no. 2, Feb. 14, 2019. [Online]. Available: https://doi.org/10.3390/catal9020179

M. C. Hidalgo, J. J. Murcia, J. A. Navío, and G. Colón, “Photodeposition of gold on titanium dioxide for photocatalytic phenol oxidation,” Applied Catalysis A: General, vol. 397, no. 1-2, Apr. 30, 2011. [Online]. Available: https://doi.org/10.1016/j.apcata.2011.02.030

J. J. Murcia, C. G. Patiño, H. A. Rojas, J. A. Navío, M. C. Hidalgo, and A. A. Botero. (2021, Oct. 13,) Photocatalytic treatment based on tio2 for a coal mining drainage. Revista Facultad de Ingeniería, Universidad de Antioquia. Medellín, ANT. [Online]. Available: https://doi.org/10.17533/udea.redin.20211063

O. Sacco, J. J. Murcia, A. E. Lara, M. Hernández-Laverde, H. Rojas, and et al., “Pt–tio2–nb2o5 heterojunction as effective photocatalyst for the degradation of diclofenac and ketoprofen,” Materials Science in Semiconductor Processing, vol. 107, Mar. 01, 2020. [Online]. Available: https://doi.org/10.1016/j.mssp.2019.104839

G. K. Upadhyay, J. K. Rajput, T. K. Pathak, V. Kumar, and L. P. Purohit, “Synthesis of zno:tio2 nanocomposites for photocatalyst application in visible light,” Vacuum, vol. 160, Feb. 2019. [Online]. Available: https://doi.org/10.1016/j.vacuum.2018.11.026

G. Iervolino, V. Vaiano, J. J. Murcia, A. E. Lara, J. S. Hernández, and et al., “Photocatalytic production of hydrogen and methane from glycerol reforming over pt/tio2–nb2o5,” International Journal of Hydrogen Energy, vol. 46, no. 78, Nov. 11, 2021. [Online]. Available: https://doi.org/10.1016/j.ijhydene.2021.09.111

A. L. Barbosa-López and I. M. Castro-Sierra, “Estudio catalítico comparativo de los sistemas tio2 y nb2o5 3h2o en la degradación de cianuro en función del tipo de oxidante,” Ingeniería y Ciencia, vol. 8, no. 16, Jul-Dec 2012. [Online]. Available: http://www.scielo.org.co/scielo.php?script=sci_arttext&pid=S1794-91652012000200010

K. Wu, X. Dong, J. Zhu, P. Wu, C. Liu, and et al., “Designing biomimetic porous celery: Tio2/zno nanocomposite for enhanced co2 photoreduction,” Journal of Materials Science, vol. 53, May. 09, 2018. [Online]. Available: https://doi.org/10.1007/s10853-018-2397-y

Standard Methods for the Examination of Water and Wastewater, American Public Health Association, American Water Works Association, Water Environment Federation, 2017.

T. Degen, M. Sadki, E. Bron, U. Konig, and G. Néner, “The highscore suite,” Powder Diffraction, vol. 29, Oct. 30, 2014. [Online]. Available: https://doi.org/10.1017/S0885715614000840

V. Vaiano, M. Matarangolo, J. J. Murcia, H. Rojas, J. A. Navío, and et al., “Enhanced photocatalytic removal of phenol from aqueous solutions using zno modified with ag,” Applied Catalysis B: Environmental, vol. 225, June 2018. [Online]. Available: https://doi.org/10.1016/j.apcatb.2017.11.075

J. J. Murcia-Mesa, L. G. Arias-Bolivar, H. A. Rojas-Sarmiento, E. G. Ávila Martínez, C. Jaramillo-Páez, and et al., “Urban wastewater treatment by using ag/zno and pt/tio2 photocatalysts,” Environmental Science and Pollution Research, vol. 26, 2019. [Online]. Available: https://doi.org/10.1007/s11356-018-1592-3

J. A. Cubillos-Lobo, J. J. Murcia-Mesa, J. R. Guarín-Romero, H. A. Rojas-Sarmiento, M. D. C. Hidalgo-López, and J. A. Navío-Santos, “Study of the visible light activity of pt and au-tio2 photocatalysts in organic pollutants degradation,” Revista Facultad de Ingeniería, Universidad de Antioquia, vol. 83, Apr. 17, 2017. [Online]. Available: https://doi.org/10.17533/udea.redin.n83a03

K. Siwińska-Stefańska, A. Kubiaka, A. Piasecki, J. Goscianska, G. Nowaczyk, and et al., “Stio2-zno binary oxide systems: Comprehensive characterization and tests of photocatalytic activity,” Materials, vol. 11, no. 5, May. 18, 2018. [Online]. Available: https://doi.org/10.3390/ma11050841

G. Pereira-Costa, R. Azevedo-Rafael, J. C. Serpa-Soares, and A. Barros-Gaspar, “Synthesis and characterization of zno-nb2o5 catalysts for photodegradation of bromophenol blue,” Catalysis Today, vol. 344, Mar. 2020. [Online]. Available: https://doi.org/10.1016/j.cattod.2019.04.059

S. M. Lam, J. C. Sin, I. Satoshi, A. Z. Abdullah, and A. R. Mohamed, “Enhanced sunlight photocatalytic performance over nb2o5/zno nanorod composites and the mechanism study,” Applied Catalysis A: General, vol. 471, Feb. 10, 2014. [Online]. Available: https://doi.org/10.1016/j.apcata.2013.12.001

L. C. Kao, W. C. Kan, R. M. Martín-Aranda, M. O. Guerrero-Perez, M. A. Bañares, and S. Y. H. Liou, “Sio2 supported niobium oxides with active acid sites for the catalytic acetalization of glycerol,” Catalysis Today, vol. 356, Oct. 2020. [Online]. Available: https://doi.org/10.1016/j.cattod.2019.08.007

N. Khadgi, A. R. Upreti, and Y. Li, “Simultaneous bacterial inactivation and degradation of an emerging pollutant under visible light by znfe2o4 co-modified with ag and rgo†,” Royal Society of Chemistry, vol. 7, May. 22, 2017. [Online]. Available: https://doi.org/10.1039/C7RA01782K

A. K. Benabbou, Z. Derriche, C. Felix, P. Lejeune, and C. Guillard, “Photocatalytic inactivation of Escherischia coli: Effect of concentration of tio2 and microorganism, nature, and intensity of uv irradiation,” Applied Catalysis B: Environmental, no. 3-4, Nov. 15, 2007. [Online]. Available: https://doi.org/10.1016/j.apcatb.2007.05.026

E. Ortega-Gómez, B. E. García, M. M. B. Martín, P. F. Ibáñez, and J. A. S. Pérez, “Inactivation of natural enteric bacteria in real municipal wastewater by solar photo-fenton at neutral ph,” Water Research, vol. 63, Oct. 15, 2014. [Online]. Available: https://doi.org/10.1016/j.watres.2014.05.034

Descargas

Publicado

2022-07-18

Cómo citar

Hernández-Niño, J. S., Murcia-Mesa, J. J. ., Rojas-Sarmiento, H. A. ., Hidalgo, M. del C., & Navío-Santos, J. A. (2022). ZnO/TiO2 y ZnO/Nb2O5 como sistemas eficientes en el tratamiento de bacterias entéricas y colorantes comerciales. Revista Facultad De Ingeniería Universidad De Antioquia, (108), 9–17. https://doi.org/10.17533/udea.redin.20220785

Número

Núm. 108 (2023): Revista Facultad de Ingeniería (Jul-Sep 2023)

Sección

Artículo de investigación

Licencia

Derechos de autor 2022 Revista Facultad de Ingeniería Universidad de Antioquia

Creative Commons License

Esta obra está bajo una licencia internacional Creative Commons Atribución-NoComercial-CompartirIgual 4.0.

Los artículos disponibles en la Revista Facultad de Ingeniería, Universidad de Antioquia están bajo la licencia Creative Commons Attribution BY-NC-SA 4.0.

Eres libre de:

Compartir — copiar y redistribuir el material en cualquier medio o formato

Adaptar : remezclar, transformar y construir sobre el material.

Bajo los siguientes términos:

Reconocimiento : debe otorgar el crédito correspondiente , proporcionar un enlace a la licencia e indicar si se realizaron cambios . Puede hacerlo de cualquier manera razonable, pero no de ninguna manera que sugiera que el licenciante lo respalda a usted o su uso.

No comercial : no puede utilizar el material con fines comerciales .

Compartir igual : si remezcla, transforma o construye a partir del material, debe distribuir sus contribuciones bajo la misma licencia que el original.

El material publicado por la revista puede ser distribuido, copiado y exhibido por terceros si se dan los respectivos créditos a la revista, sin ningún costo. No se puede obtener ningún beneficio comercial y las obras derivadas tienen que estar bajo los mismos términos de licencia que el trabajo original.

Crossref
Scopus
Google Scholar
Europe PMC

Artículos más leídos del mismo autor/a

1. Introduction

Municipal wastewater released into natural water sources currently represents a critical problem worldwide. This is primarily because high volumes of water are being polluted every day, leading to a decrease in the availability of this natural resource for human consumption, agricultural use, and domestic activities [1,2]. As a result, the current study attempted to search for new ways to treat and recover wastewater.

In the last decade, Advanced Oxidation Processes (AOPs) have been widely studied to achieve this objective [3-5]. The effectiveness of these technologies is based on the generation of strong and non-selective radicals, leading to the elimination of a wide variety of contaminants and enteropathogenic bacteria present in wastewater [6-9]. The most common AOPs used for the treatment of wastewater are solar photo-Fenton, solar UV-Vis/H2O2, UV/O3, and solar photocatalysis based on semiconductors such as ZnO or TiO2.

In general, heterogeneous photocatalysis based on semiconductors leads to a photochemical activation process that can be applied to a wide variety of reactions such as total oxidations, hydrogen transfer, dehydrogenation, metal deposition, water detoxification, and the removal of gaseous pollutants, among others[10]. The activation of the semiconductor enables the promotion of an electron from the valence band to the conduction band. This process simultaneously creates a hole with a positive charge density which is generated in the valence band, as shown in Equation 1.

These photogenerated charges have an important influence on the elimination of pollutants by AOPs. Even though the effectiveness of these treatments has been proven in different environmental recovery processes, heterogeneous photocatalysis presents a series of disadvantages. For instance: in this process, the 𝑒− + ℎ+ pair can be recombined in nanoseconds, thus leading to a significant decrease in the overall treatment effectiveness. In order to avoid this recombination, different methodologies such as the addition of fluorine [11] and the photodeposition of metal nanoparticles including Au, Ag, and Pt have been employed [4,12].

It has also been reported that the heterojunction formation between mixed oxides such as ZnO, TiO2, and Nb2O5 is an effective way to achieve a better separation of photogenerated charges. This improves the photocatalytic response of these materials [13], and therefore, the effectiveness of the composed materials in wastewater treatment by photocatalytic processes [13-15].

It is also widely known that Nb2O5 has basic acid properties, which can effectively contribute to the degradation of different organic pollutants like dyes, glycerol, cyanide, bacteria, and drugs 14,16-18. This effect can be associated with better adsorption of these pollutants on the surface of niobia, which can present positive and or negative active sites available for its adsorption, thus leading to a more effective way of breaking the bonds in the pollutant molecule.

From the perspective of the current study, it is possible to observe that a number of scientific studies have been devoted to the evaluation of the efficiency of mixed oxides in the degradation of organic pollutants; however, most of these studies are focused on the use of lab prepared solutions including model molecules as substrates. Currently, there is an important necessity in the evaluation of treatments as potential answers to solve environmental problems. As a result, it is very important to know the effectiveness of different treatments by using real wastewater.

Taking the above into account, the main objective of this study was to test the effectiveness of heterojunctions formed by ZnO/TiO2 and ZnO/Nb2O5 in the photocatalytic treatment of real wastewater samples. These polluted samples were obtained from textile fiber dyeing activities in handicraft factories and water samples from a polluted river. The photocatalytic performance of these heterojunctions for the elimination of organic pollutants such as dyes and the elimination of bacteria such as E. Coli was evaluated.

2. Materials and methods

2.1 Photocatalysts preparation

The prepared materials corresponding to heterojunctions were formed by coupling pairs of oxides. These materials were prepared following the wet impregnation method reported by Vaiano et al. [14]. The TiO2 (Sigma Aldrich, 99.7%) and Nb2O5 (Sigma Aldrich, 99.9%) with commercial ZnO (Sigma Aldrich, 99.0%) were mixed in a defined 1:1 ratio. This mixture was subjected to rotatory evaporation in the presence of an isopropanol solution (0.3M) for 1 hour at 82 ºC. Finally, the materials were recovered by centrifugation and characterized by different instrumental analysis techniques.

2.2 Photocatalyst characterization

The materials prepared were characterized by XRD, SBET, and UV-Vis DRS. The experimental conditions of these analyses and the equipment employed are described as follows. The XRD analyses were carried out by using a Siemens D-501 diffractometer, including a nickel filter and cupper Kα radiation. The scanning angle utilized was 2θ from 10° to 80° with passes of 0.05° and a total lecture time of 1 s. The photocatalysts were evaluated by UV-Vis diffuse reflectance spectrophotometry (UV-Vis DRS) by using a Varian Cary 100 spectrophotometer with an integrating sphere and BaSO4 as a reference. These measurements were evaluated in a wavelength range between 200 and 800 nm. The band gap values were calculated by using the Kubelka-Munk F(R∞) function, which is proportional to the absorption of radiation. These calculations utilized the graphical function (F(R∞) × hν)1/2 Vs. hν.

2.3 Wastewater sampling

The water samples to be treated by photocatalysis were collected from two different sources and are described as follows: (i) In Tunja, Colombia, from a highly polluted river due to municipal effluents which was sampled at the coordinates 5° 33' 13.5" N, 73° 21' 02.6" W; and (ii) at a textile factory located in Nobsa, Colombia, at the coordinates 5°46′11″ N, 72°56′24″ W. The samples were collected in batches of 30 L, transported and stored using the protocols described in the Standard Methods for Examination of Water and Wastewater (SMEWW) [19]. The samples were tested on the same day they were collected.

The water samples were characterized before and after photocatalytic treatment. Hardness, alkalinity, and chlorine concentration were determined according to the Standard Methods[19], as reported in Table 1. TOC analyzes were performed using an AJ multi N/C series TOC analyzer. The Total Coliforms and E. Coli colonies were determined using the standard plate count method with dilutions in a selective Chromocult (26.5 g/L Merck Agar Chromocult) medium. Colonies were counted after 24 hours of incubation at 37º C. The bacteria concentration in the wastewater samples analyzed is reported as CFU (Colony Forming Units)/ 100 mL. Bacterial regrowth studies were conducted and monitored every 24 hours for three days.

The pH values were measured by using an SI analytics Lab 850 pH meter. Other physicochemical parameters such as alkalinity, hardness, and chloride content were calculated by using the 2320 B-1995 APHA, 2340: C APHA, and 4500 Cl-B-1995 APHA methods, respectively[19]. All of the physicochemical analyzes were carried out twice.

The evaluation of the dye concentrations in the handicraft factories’ wastewater during the photocatalytic tests was analyzed by UV-Vis spectrophotometry using a Thermo Scientific Evolution 300 spectrophotometer.

2.4 Wastewater photocatalytic treatment

Photocatalytic tests were carried out in a batch reactor using a 200 mL sample of wastewater, 1 g/L of photocatalysts, an oxygen flow of (50 L/h), and a total treatment time of 240 minutes under continuous magnetic stirring. As a light source to induce the photocatalytic reaction, an Osram Ultravitalux lamp (300W) with radiation similar to sunlight and the main emission at 365 nm was used. In order to promote the adsorption-desorption equilibrium in the suspension (water sample - photocatalyst), some procedures were carried out. Thus, before switching on the light, it was maintained under stirring and air flow, in the dark, for 10 minutes.

XRD Patterns for the photocatalysts analyzed

Figure 1: XRD Patterns for the photocatalysts analyzed

The main conditions employed for the heterogeneous photocatalysis processes are enlisted as follows: (i) All reactions were carried out at room temperature (20 + 1 ºC), (ii) under atmospheric pressure, (iii) the photocatalysis dose was 1 g/L and (iv) total reaction time of 4 hours.

Finally, in order to obtain confident experiments, all photocatalytic experiments were carried out twice.

3. Results and discussion

3.1 Characterization results

The XRD spectra for the semiconductors analyzed in this study are shown in Figure 1. As can be seen, the diffraction pattern of ZnO indicates the wurtzite structure for this semiconductor, with an average crystal size of around 25 nm [9,18]. The main signal for TiO2 is observed around 2θ = 25.25°, which indicates the presence of only the Anatase crystalline phase for this material [4,18]. In the case of Nb2O5, the main signal can be observed around 2θ = 28.58° due to the plane (100), corresponding to the crystalline Nb2O5 in the hexagonal phase [13,18].

Table 1:
Physicochemical and microbiological average values of wastewater samples

UV-Vis DRS spectra of the photocatalysts analyzed

Figure 2: UV-Vis DRS spectra of the photocatalysts analyzed

The diffraction patterns of mixed oxides show three maindiffraction signals located at 2θ = 31.7°, 34.5°, and 36.2°, corresponding to planes (100), (002), and (101) of ZnO in the Wurtzite crystalline phase [17]. In the ZnO/TiO2 material, a diffraction signal around 2θ = 25.25° can be observed, it is associated to the main of the Anatase crystalline phase of TiO2 [20,21]. In the ZnO/Nb2O5 diffraction pattern, a band around 2θ = 28°, characteristic of the pure hexagonal phase Nb2O5 [14] is seen. These results suggest that the synthesis method used for the preparation of mixed oxides did not modify the crystallinity of the pristine semiconductors.

The TiO2 photocatalyst presents a low surface area (SBET), with a value of 11 m2/g when compared with ZnO (30.20 m2/g). On the other hand, the UV-Vis DRS spectra of TiO2 and ZnO are presented in Figure 2. The absorbance spectra seen by the characteristic absorption edge of the ZnO, TiO2, and Nb2O5 photocatalysts are located around 400 nm. This band is associated with the intrinsic transition in these photocatalysts. The band gap energy calculated for the photocatalysts were 3.25 eV, 3.33 eV, 3.25 eV, 2.95 eV, and 3.02 for ZnO, Nb2O5, TiO2, ZnO/TiO2, and ZnO/ Nb2O5, respectively.

3.2 Photocatalytic wastewater treatment

Polluted river water

The results obtained in eliminating bacteria present in the river under study are summarized in Table 2. Municipal wastewater treatment using ZnO/TiO2 and ZnO/Nb2O5 photocatalysts was moderately effective in the elimination of bacteria. Using the unmodified oxides, 50% effectiveness of the treatment is not exceeded, while with the materials ZnO/TiO2 and ZnO/Nb2O5, and elimination percentages of 55.5% and 64%, respectively, were achieved after 240 reaction minutes which increased over time. This may be because the coupling of two semiconductor materials extends the half-life of the hollow electron pair. The electrons photogenerated in the surface of one of the oxides can jump to the conduction band of the others and involve reduction reactions to produce reactive radicals that react with the pollutant generating its degradation. Additionally, the free holes in the system can react with -OH or water, promoting the production of •OH, which is the main radical responsible for the oxidation of organic molecules until the formation of CO2 and H2O [21,22].

Figure 3 shows the TOC results, which demonstrate the coupling of semiconductors in order to increase the mineralization of the pollutant. When the reaction is carried out by using ZnO, TiO2, and Nb2O5, the TOC elimination percentage was 42.3%, 48.49%, and 57.25%, respectively. However, using ZnO/Nb2O5, an 83% elimination of organic material present in contaminated river water samples was achieved.

Likewise, the figure shows that the coupling of ZnO with TiO2, in this case, does not work as expected because the removal of TOC with this photocatalyst only reached 33%. This is due mainly to the band gap energy of the photocatalysts, especially since ZnO/Nb2O5 showed the lowest value (2.95 eV), which allows the electrons to be photogenerated with lower energy on the surface of the material as well as presenting Lewis acids sites on the surface. Niobia could act as an electron collector, which increases the half-life time of the photogenerated charges and this leads to better photocatalytic performance [22-24].

Table 2:
Bacteria elimination in river water samples using mixed oxides

Table 3:
Physicochemical average values of wastewater samples from textile handicrafts factories
Photocatalyst Reaction time (min) Hardness (mg/L CaCO3) Alkalinity (mg/L CaCO3) Chlorides (mg/L Cl-) pH
ZnO 0 330 3202.78 5672.48 8.983
240 320 3122.71 5495.21 8.674
TiO2 0 300 3202.78 5672.48 8.983
240 310 3202.78 5672.48 8.894
Nb2O5 0 330 3202.78 5672.48 8.983
240 320 3122.71 5495.21 9.095
ZnO/TiO2 0 330 3202.78 5672.48 8.983
240 300 3202.78 5495.21 9.074
ZnO/ Nb2O5 0 330 3202.78 5672.48 8.983
240 320 2962.57 5495.21 9.063

TOC results of evaluated photocatalysts
Figure 3: TOC results of evaluated photocatalysts

Total coliforms elimination after 240 reaction minutes using the photocatalysts ZnO/TiO2 and ZnO/Nb2O5
Figure 4: Total coliforms elimination after 240 reaction minutes using the photocatalysts ZnO/TiO2 and ZnO/Nb2O5

Dyes photodegradation in wastewater samples from textile handicraft factories
Figure 5: Dyes photodegradation in wastewater samples from textile handicraft factories

Wastewater from textile fiber staining activities in handicrafts factories

Figure 4 shows the results of the bacteria elimination in the wastewater samples from textile handicrafts factories. From the figure, the composite materials showed greater effectiveness for the elimination of bacteria than the unmodified materials (ZnO, Nb2O5, and TiO2), with ZnO/Nb2O5 being the best material for the elimination of microorganisms with an elimination percentage of 71% after 240 reaction minutes. Although it is a relatively high percentage for the elimination of bacteria, the large amount of CFU that persists in the sample after the reaction must be considered since microorganisms proliferate easily under normal conditions of temperature and pressure. This increased performance for the elimination of pathogenic bacteria in these samples is mainly due to the initial population in the sample (6000 CFU / 100 mL) in comparison with the water from the polluted river (37800 CFU / 100 mL). On the other hand, it is important to note that these wastewater samples present higher TOC values and physicochemical parameters such as alkalinity, hardness, and chlorides. These values were greater in comparison with the polluted river water samples, as reported in Table 3. Recent research has mentioned that the high concentration of salt species in the reaction medium decreases the possibility of finding photogenerated holes in the system that will interact with O2 or -OH species in order to produce •OH, which have been identified as being primarily responsible for the elimination of bacteria [4,25-27].

The results obtained in the elimination of dyes on unmodified materials were studied by UV-Vis Spectroscopy; these results are presented in Figure 5. These semiconductors show photocatalytic activity for the elimination of dyes in the wastewater samples; however, the elimination of color is only 33.3%, 81%, and 78% for Nb2O5. ZnO, and TiO2, respectively. This result is mainly due to the lower photogeneration of ROS on the surface of pristine oxides compared to the heterojunctions formed [14,22,24,28]. In the case of Nb2O5, as previously reported, it can have repulsive effects on dyes such as bromophenol blue (BPB), preventing this dye from being degraded [25]. The improved efficiency for the elimination of bacteria can be attributed to the efficiency of the separation of the charge carriers and the quantity of photogenerated ROS. Additionally, the presence of Zn2+ in the prepared materials could enter into the bacterial membrane and promote the proliferation of fibroblasts, thus providing a long-lasting antibacterial property [29], and, finally, the inactivation of the bacteria.

The mixed oxides make it possible to significantly increase the dyes elimination in solution. The elimination percentages obtained were 91% and 90% for ZnO/TiO2 and ZnO/Nb2O5, respectively. Although the percentages of dye removal are significant, it should be noted that the coupling of ZnO with Nb2O5 allowed the drawbacks regarding the affinity of the latter for dyes to be overcome, increasing the photocatalytic material response. These results are due to a decreased energy bandwidth, unchanged crystallinity of the materials, and improved light absorption properties, as evidenced in the characterization of the samples. It has been previously reported that the high efficiency of the materials can be due to the cascade effect of the photogenerated carriers during the separation of the electron-hole pair, the transfer to the other semiconductor, and the migration to the surface of heterojunction formed that permits the oxidation-reduction reactions to be carried out. These characteristics allow the elimination of the organic pollutants present in the wastewater samples to be effective [30].

4. Conclusions

The coupling of ZnO with oxides such as TiO2 and Nb2O5 proved to be a suitable methodology to increase their effectiveness in photocatalytic treatments. This is because these kinds of nanocomposites resulted in an effective separation of photogenerated charges. The ability for photogenerated electrons and holes, which can jump into the conduction or valence band of the other semiconductor, allows them to be more involved in oxidation-reduction reactions to encourage the production of ROS, thereby making photocatalytic treatments more effective.

The mixed oxide that exhibited the best behavior for the elimination of pathogenic microorganisms, degradation of dyes, and photo-reduction of metals was ZnO/Nb2O5. This is due to the physicochemical properties it showed during its characterization: i) Lower bandwidth energy (2.95 eV) with respect to starting materials, ii) high crystallinity in the material, and iii) homogeneity in the distribution and particle size of the material.

Acknowledgements

Acknowledgements

The Universidad Pedagógica y Tecnológica de Colombia (UPTC) is acknowledged for the financial support of this study. J.S. Hernandez would like to thank VIE-UPTC for financing the project SGI 3021.

References

  1. , (). . . Geneva, SWE: World Health Organization, UNICEF. .
  2. (). . (14). .
  3. , (). Antimicrobial and photocatalytic disinfection mechanisms in silver-modified photocatalysts under dark and light conditions. Journal of Photochemistry and Photobiology C: Photochemistry Reviews 19
  4. , , , , (). Study of the E. coli elimination from urban wastewater over photocatalysts based on metallized tio2. Applied Catalysis B: Environmental 200
  5. , , , , (). Solar photocatalysis as a tertiary treatment to remove emerging pollutants from wastewater treatment plant effluents. Applied Catalysis B: Environmental 161(1)
  6. , , , , (). Decontamination and disinfection of water by solar photocatalysis: Recent overview and trends. Catalysis Today 147(1)
  7. , , , (). High uv-photocatalytic activity of zno and ag/zno synthesized by a facile method. Catalysis Today 284
  8. , , , , (). Uv and visible-light driven photocatalytic removal of caffeine using zno modified with different noble metals (pt, ag and au). Materials Research Bulletin 112
  9. , , , (). Zno and pt-zno photocatalysts: Characterization and photocatalytic activity assessing by means of three substrates. Catalysis Today 313
  10. (). Heterogeneous photocatalysis: fundamentals and applications to the removal of various types of aqueous pollutants. Catalysis Today 53(1)
  11. , , , , , (). Fluorinated and platinized titania as effective materials in the photocatalytic treatment of dyestuffs and stained wastewater coming from handicrafts factories. Catalysts 9(2)
  12. , , , , (). Photodeposition of gold on titanium dioxide for photocatalytic phenol oxidation. Applied Catalysis A: General 397(1-2)
  13. , , , , , (). Photocatalytic treatment based on tio2 for a coal mining drainage. Revista Facultad de Ingeniería, Universidad de Antioquia
  14. , , , , , (). Pt-tio2-nb2o5 heterojunction as effective photocatalyst for the degradation of diclofenac and ketoprofen. Materials Science in Semiconductor Processing 107
  15. , , , , (). Synthesis of zno:tio2 nanocomposites for photocatalyst application in visible light. Vacuum 160
  16. , , , , , (). Photocatalytic production of hydrogen and methane from glycerol reforming over pt/tio2-nb2o5. International Journal of Hydrogen Energy 46(78)
  17. , (). Estudio catalítico comparativo de los sistemas tio2 y nb2o5 3h2o en la degradación de cianuro en función del tipo de oxidante. Ingeniería y Ciencia 8(16)
  18. , , , , (). Designing biomimetic porous celery: Tio2/zno nanocomposite for enhanced co2 photoreduction. Journal of Materials Science 53
  19. , , (). . . .
  20. , , , , (). The highscore suite. Powder Diffraction 29
  21. , , , , (). Enhanced photocatalytic removal of phenol from aqueous solutions using zno modified with ag. Applied Catalysis B: Environmental 225
  22. , , , , (). Urban wastewater treatment by using ag/zno and pt/tio2 photocatalysts. Environmental Science and Pollution Research 26
  23. , , , , , (). Study of the visible light activity of pt and au-tio2 photocatalysts in organic pollutants degradation. Revista Facultad de Ingeniería, Universidad de Antioquia 83
  24. , , , , (). Stio2-zno binary oxide systems: Comprehensive characterization and tests of photocatalytic activity. Materials 11(5)
  25. , , , (). Synthesis and characterization of zno-nb2o5 catalysts for photodegradation of bromophenol blue. Catalysis Today 344
  26. , , , , (). Enhanced sunlight photocatalytic performance over nb2o5/zno nanorod composites and the mechanism study. Applied Catalysis A: General 471
  27. , , , , , (). Sio2 supported niobium oxides with active acid sites for the catalytic acetalization of glycerol. Catalysis Today 356
  28. , , (). Simultaneous bacterial inactivation and degradation of an emerging pollutant under visible light by znfe2o4 co-modified with ag and rgo†. Royal Society of Chemistry 7
  29. , , , , (). Photocatalytic inactivation of Escherischia coli: Effect of concentration of tio2 and microorganism, nature, and intensity of uv irradiation. Applied Catalysis B: Environmental (3-4)
  30. , , , , (). Inactivation of natural enteric bacteria in real municipal wastewater by solar photo-fenton at neutral ph. Water Research 63
* Data availability statement: The samples were collected from an anonymous handicraft factory in batches of 30 L, transported and stored using the protocols described in the Standard Methods for Examination of Water and Wastewater, and these were tested on the same day they were collected. All the test were measure to duplicate in order to guarantee the reproducibility of the research. The data was obtained in February to June 2020 by catalysis laboratory of UPTC. The data is available upon request.
* Cite this article as: J. S. Hernández, J. J. Murcia,H. Rojas, M. C. Hidalgo and J.A. Navío ”ZnO/T iO2andZnO/N b2O5as effective systems for the treatment of enteric bacteria and commercial dyes”,Revista Facultad de Ingeniería Universidad de Antioquia, no.108, pp. 9-17, Jul-Sep 2023. [Online]. Available: https://www.doi.org/10.17533/udea.redin.20220785
Funding: This study was supported by Universidad Pedagógica y Tecnológica de Colombia (UPTC) and Vicerrectoria de investigaciones VIE-UPTC