Polyurethane flexible foam recycling via glycolysis using Zn/Sn/Al hydrotalcites as heterogeneous catalyst
DOI:
https://doi.org/10.17533/udea.redin.n87a10Keywords:
polyurethane, chemical recovery, Zn/Sn/Al catalyst, compression tests, polyol, foam wastesAbstract
Polyurethane is a highly versatile material used in comfort, packaging and isolation industries. The global production of polyurethane generates several million tons of non-biodegradable wastes. In this research, the chemical recovery of polyol from polyurethane flexible foam (PUF) wastes was explored. The polyol recovery from PUF was carried out via glycolysis with diethylene glycol (DEG) as a glycolysis agent, Zn/Sn/Al hydrotalcite (HTC) as a heterogeneous catalyst under inert atmosphere using several reaction conditions. The most suitable reaction conditions were achieved for 3 h of reaction, PUF/DEG mass ratio of 1.5 and HTC/DEG of 0.001. The HTC was characterized by FTIR, XRD, TEM and chemical analysis. The recovered polyol was characterized using IR, viscometry and GPC; density and water content was also determined. The recovered polyol was used in the synthesis of PUF as a partial replacement of virgin polyols, and the resultant foams were analyzed using compression tests.
Downloads
References
C. Defonseka, “Propiertes and Foaming Technology of Polyurethane Foam,” in Practical Guide to Flexible Polyurethane Foams. United Kingdom: Smithers Rapra Technology, 2013, pp. 58–60.
M. M. Alavi, “Brief Review of the Methods of Recycling of Polyurethane Foam Wastes,” in Recycling of Polyurethane Wastes. United Kingdom: Smithers Rapra, 2016, pp. 13–48.
H. Ulrich, A. Odinak, B. Tucker, and A. A. R. Sayigh, “Recycling of Polyurethane and Polyisocyanurate foam,” Polymer Engineering & Science, vol. 18, no. 11, pp. 844–848, Aug. 1978.
M. Murai, M. Sanou, T. Fujimoto, and F. Baba, “Glycolysis of Rigid Polyurethane Foam under Various Reaction Conditions,” J. Cell. Plast., vol. 39, no. 1, pp. 15–27, Jan. 2003.
M. M. Alavi and F. H. A. Mohammadi, “Sorbitol/glycerin/water ternary system as a novel glycolysis agent for flexible polyurethane foam in the chemical recycling using microvawe radiation,” Polimery, vol. 54, no. 7-8, pp. 541–545, 2009.
M. M. Alavi, M. Haghshenas, and A. B. Garmarudi, “Glycolysis of Waste Polyurethane Integral Skin Foams from Steering Wheel,” Polym. Plast. Technol. Eng., vol. 45, no. 4, pp. 569–573, Feb. 2006.
C. Molero, A. de Lucas, and J. F. Rodríguez, “Recovery of polyols from flexible polyurethane foam by ’split-phase’ glycolysis with new catalysts,” Polymer Degradation and Stability, vol. 91, no. 4, pp. 894–901, Apr. 2006.
C. H. Wu, C. Y. Chang, C. M. Cheng, and H. C. Huang, “Glycolysis of waste flexible polyurethane foam,” Polym. Degrad. Stab., vol. 80, no. 1, pp. 103–111, 2003.
C. Molero, A. de Lucas, F. Romero, and J. F. Rodríguez, “Glycolysis of flexible polyurethane wastes using stannous octoate as the catalyst,” Journal of Material Cycles and Waste Management, vol. 11, no. 2, pp. 130–132, May 2009.
D. Simón, M. T. García, A. de Lucas, A. M. Borreguero, and J. F. Rodríguez, “Glycolysis of flexible polyurethane wastes using stannous octoate as the catalyst: Study on the influence of reaction parameters,” Polymer Degradation and Stability, vol. 98, no. 1, pp. 144–149, Jan. 2013.
M. Zhu, S. Li, Z. Li, X. Lu, and S. Zhang, “Investigation of solid catalysts for glycolysis of polyethylene terephthalate,” Chemical Engineering Journal, vol. 185-186, pp. 168–177, Mar. 2012.
M. Zhu, Z. Li, Q. Wang, X. Zhou, and X. Lu, “Characterization of Solid Acid Catalysts and Their Reactivity in the Glycolysis of Poly(ethylene terephthalate,” Ind. Eng. Chem. Res., vol. 51, no. 36, pp. 11 659–11 666, Aug. 2012.
F. Chen, F. Yang, G. Wang, and W. Li, “Calcined Zn/Al hydrotalcites as solid base catalysts for glycolysis of poly(ethylene terephthalate),” J. Appl. Polym. Sci., vol. 131, pp. 1–10, Jun. 2014.
C. Molero, A. D. Lucas, and J. F. Rodríguez, “Recovery of polyols from flexible polyurethane foam by ’split-phase’ glycolysis: Study on the influence of reaction parameters,” Polymer Degradation and Stability,, vol. 93, no. 2, pp. 353–361, Feb. 2008.
T. Wang, Z. Yang, B. Yang, R. Wang, and J. Huang, “The electrochemical performances of Zn-Sn-Al-hydrotalcites in Zn-Ni secondary cells,” Journal of Power Sources, vol. 257, no. 36, pp. 174–180, Jul. 2014.
R. Wang, Z. Yang, B. Yang, and T. W. Chu, “Superior cycle stability and high rate capability of Zn-Al-In-hydrotalcite as negative electrode materials for Ni-Zn secondary batteries,” Journal of Power Sources, vol. 251, pp. 344–350, Apr. 2014.
N. H. et al, “Modeling of glycolysis of flexible polyurethane foam wastes by artificial neural network methodology,” Polymer International, vol. 64, no. 9, pp. 1111–1120, Jan. 2015.
Standard Test Method for Polyurethane Raw Materials : Determination of Specific Gravity of Polyols 1 TEST METHOD A — SPECIFIC GRAVITY USINGA, ASTM Compass, 2017.
E. M. Ravei and M. Pearce, “Flexible Polyurethane Foam .L. Thermal Decomposition of a Polyether-based, Water-blown Commercial Type of Flexible Polyurethane Foam,” Journal of Applied Polymer Science, vol. 63, no. 1, p. 47–74, Dec. 1998.
F. Bruma, “Application of hydrotalcites as adsorbents for the reduction of contamination by water and soil pesticides,” M.S. thesis, University of Cordoba. Science Faculty, Monteria, Colombia, 2010.
C. A. Antonyraj, P. Koilraj, and S. Kannan, “Synthesis of delaminated LDH: A facile two step approach,” Chem. Commun., vol. 46, no. 11, pp. 1902––1904, Jan. 2010.
K. Okamoto, N. Iyi, and T. Sasaki, “Factors affecting the crystal size of the MgAl-LDH (layered double hydroxide) prepared by using ammonia-releasing reagents,” Applied Clay Science, vol. 37, no. 1-2, pp. 23–31, Jun. 2007.
K. Abderrazek, N. F. Srasra, and E. Srasra, “Synthesis and Characterization of [Zn-Al] Layered Double Hydroxides: Effect of the Operating Parameters,” Journal of the Chinese Chemical Society, vol. 64, no. 3, pp. 346–353, Feb. 2017.
M. Geetanjali, D. Barsha, S. Diptipriya, P. Sony, and B. K. Mishra, “Orientation of Organic Anions in Zn-Al Layered Double Hydroxides with Enhanced Antibacterial Property,” Environmental Engineering Science, vol. 34, no. 7, pp. 516–527, Jul. 2017.
BASF. (2015) Safety Sheet PLuRACOL 4156 POLYOL. Accessed Nov. 9, 2017. [Online]. Available: https: //worldaccount.basf.com/wa/{N}{A}{F}{T}{A}~en_{U}{S}/{C}atalog/ {P}olyurethane/info/{B}{A}{S}{F}/{P}{R}{D}/30426020.
S. P. Technology. (2017) BASF Pluracol 4156 Slabstock Foam Polyol. Accessed Nov. 9, 2017. [Online]. Available: http://www.matweb.com/search/{Data}{Sheet}.aspx?{M}at{G}{U}{I}{D}=225071fd65a04f929a34122ec3e9e7cf&ckck=1.
M. M. Alavi, M. Haghshenas, and A. B. Garmarundi, “Glycolysis of waste polyurethane integral skin foams from sterring wheel,” Polymer-Plastics Technology and Engineering, vol. 45, no. 4, pp. 569–573, Feb. 2006.
D. Simón, A. de Lucas, J. F. Rodríguez, and A. M. Borreguero, “Glycolysis of high resilience flexible polyurethane foams containing polyurethane dispersion polyol,” Polymer Degradation and Stability. Syst., vol. 133, pp. 119–130, Nov. 2016.
P. C. Painter and M. M. Coleman, “Polymer science fundamentals,” in Nature of polymeric materials. Pensilvania: Technomic Publishing Company, 1996, p. 22.
M. C. Gutiérrez, A. Burdó, and J. Cegarra, “Chromatography of exclusion: Analysis of the distribution of molecular weights in silicones by GPC,” INTEXTER BULLETIN (U.P.C.), no. 135, pp. 33–40, 2009.
D. V. W. M. D. Vries, “Characterization of polymeric foams,” M.S. thesis, Eindhoven University of Technology, Netherlands, Eindhoven, 2009.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2018 Revista Facultad de Ingeniería Universidad de Antioquia
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.
Revista Facultad de Ingeniería, Universidad de Antioquia is licensed under the Creative Commons Attribution BY-NC-SA 4.0 license. https://creativecommons.org/licenses/by-nc-sa/4.0/deed.en
You are free to:
Share — copy and redistribute the material in any medium or format
Adapt — remix, transform, and build upon the material
Under the following terms:
Attribution — You must give appropriate credit, provide a link to the license, and indicate if changes were made. You may do so in any reasonable manner, but not in any way that suggests the licensor endorses you or your use.
NonCommercial — You may not use the material for commercial purposes.
ShareAlike — If you remix, transform, or build upon the material, you must distribute your contributions under the same license as the original.
The material published in the journal can be distributed, copied and exhibited by third parties if the respective credits are given to the journal. No commercial benefit can be obtained and derivative works must be under the same license terms as the original work.
Twitter